Function introduction
HARDOX 400 is a Brinell hardness of 400HB wear-resistant steel plate, with good cold bending, mainly used in anti-wear conditions. The HARDOX 400 has excellent weldability.
HARDOX400 wear-resistant steel applications: crusher, screen plate, feeder, feeding funnel, elevator, blade plate, conveyor, bucket, knife plate, gear, dump truck, scraper, industrial truck, railway freight car, bulldozer, excavator. Slurry pipe, screw conveyor, press, etc.
HARDOX400 wear-resistant steel is: "Fine-grained steel"
HARDOX400 wear-resistant steel hardness: 370-430HBW.
HARDOX400 wear-resistant steel mechanical properties: yield strength Re=1000MPa. Tensile strength Rm=1250MPa. Elongation A5=10% (typical value of 20 mm thickness steel plate).
Impact toughness of HARDOX400 wear-resistant steel: Test temperature: -40 (-40F) ℃. Impact power Charpy-V longitudinal =45J (typical value of 20 mm thick steel plate).
HARDOX400 Handa wear-resistant steel delivery status: quenched.
Implementation standard for HARDOX400 wear-resistant steel: EN 10 204-3.1.
product presentation
HARDOX wear-resistant steel plates are divided into: HARDOX wear-resistant 400, HARDOX wear-resistant 450, HARDOX wear-resistant 500, HARDOX wear-resistant 550, HARDOX wear-resistant 600 and HARDOX wear-resistant HiTuf. This means that you can always find a HARDOX steel plate that meets your specific needs.
The HARDOX Solder 400 and HARDOX Solder 450 are versatile wear plates. Due to its high toughness, good bending and welding properties, it can also be used for bearing purposes in some applications.
The HARDOX 500 is a bendable and weldable wear-resistant plate that can be used in applications that require higher wear resistance.
HARDOX 550 is a wear-resistant steel plate with an average hardness of 550HBW, and its toughness is the same as HARDOX 500, which is used in high-wear applications. It is mainly aimed at users and manufacturers using high manganese steel castings or wear-resistant steel plates with Brinell hardness of 500. When upgraded from the HARDOX 500 steel plate to this product, the Brinell hardness is increased by 50 units, extending the wear life without losing the toughness of the steel plate. Read more: HARDOX to 550, HARDOX to 550 in the Workshop
HARDOX 600 is the hardest wear resistant steel in the world with a hardness of 600HBW. It is generally used in extremely severe wear situations, and is mainly used to replace cast steel, chromium alloy cast iron and surface hardened metals. Despite its high hardness, we are able to machine, weld and cut it. Although HARDOX has a very high hardness of up to 600, it still has a fairly high impact toughness.
WEAR-RESISTANT STEEL PLATE
The Materials, Grades, Standards, Dimensions supplied in the below list